Three requirements for selecting metal mold materials

2021-12-21 15:48:07
times

When choosing hardware mold materials, experts suggest that the focus should be on whether it can meet the following three requirements:


(1) The mold meets the economic requirements


In the selection of mold materials, the principle of economy must be considered to reduce manufacturing costs as much as possible. Therefore, under the premise of satisfying the performance, first choose the lower price, if you can use carbon steel, you don't need alloy steel, and if you can use domestic materials, you don't need imported materials. In addition, the production and supply situation in the market should also be considered when selecting materials. The selected steel grades should be as few and concentrated as possible and easy to purchase.


(2) The mold meets the requirements of working conditions


1. Strength and toughness: Most of the working conditions of the mold are very bad, and some often bear a large impact load, which leads to brittle fracture. In order to prevent sudden brittle fracture of mold parts during operation, the mold must have high strength and toughness. The toughness of the mold mainly depends on the carbon content, grain size and organizational state of the material.


2. Fatigue fracture performance: During the working process of the mold, under the long-term action of cyclic stress, fatigue fracture is often caused. Its forms include small-energy multiple impact fatigue fracture, tensile fatigue fracture, contact fatigue fracture and bending fatigue fracture. The fatigue fracture performance of the mold mainly depends on its strength, toughness, hardness, and the content of inclusions in the material.


3. High temperature performance: When the working temperature of the mold is high, the hardness and strength will decrease, resulting in early wear of the mold or plastic deformation and failure. Therefore, the mold material should have high anti-tempering stability to ensure that the mold has high hardness and strength at working temperature.


4. Heat and cold fatigue resistance: some molds are in a state of repeated heating and cooling during the working process, which causes the surface of the cavity to be stretched and the pressure changes stress, causing surface cracking and peeling, increasing friction and hindering plastic deformation. , reducing the dimensional accuracy, resulting in mold failure. Hot and cold fatigue is one of the main forms of failure of hot work dies, and these dies should have high resistance to cold and heat fatigue.


5. Corrosion resistance: When some molds such as plastic molds are working, due to the presence of chlorine, fluorine and other elements in the plastic, strong corrosive gases such as HCI and HF are decomposed after heating, which erodes the surface of the mold cavity and increases its surface roughness. degree, aggravating wear failure.


6. Wear resistance: When the blank is plastically deformed in the mold cavity, it both flows and slides along the surface of the cavity, causing severe friction between the surface of the cavity and the blank, resulting in the failure of the mold due to wear. Therefore, the wear resistance of the material is one of the most basic and most important properties of the mold.


Hardness is the main factor affecting wear resistance. In general, the higher the hardness of the mold parts, the smaller the amount of wear and the better the wear resistance. In addition, wear resistance is also related to the type, quantity, shape, size and distribution of carbides in the material.


(3) The mold meets the process performance requirements


The manufacture of molds generally has to go through several processes such as forging, cutting, and heat treatment. In order to ensure the manufacturing quality of the mold and reduce the production cost, the material should have good forgeability, machinability, hardenability, hardenability and grindability; it should also have small oxidation, decarburization sensitivity and quenching properties. Deformation and cracking tendency.


1. Hardenability: It has uniform and high surface hardness after quenching.


2. Machinability: large cutting amount, low tool loss and low surface roughness.


3. Hardenability: After quenching, a deep hardened layer can be obtained, which can be hardened by using a mild quenching medium.


4. Annealing manufacturability: The spheroidizing annealing temperature range is wide, the annealing hardness is low and the fluctuation range is small, and the spheroidization rate is high.


5. Forgeability: low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency for forging cracking and cold cracking and precipitation of network carbides.


6. Sensitivity to oxidation and decarburization When heated at high temperature, it has good oxidation resistance, slow decarburization rate, insensitivity to heating medium, and small tendency to produce pitting.


7. Grindability: The relative loss of the grinding wheel is small, the limit grinding amount without burn is large, it is not sensitive to the quality of the grinding wheel and the cooling conditions, and it is not easy to cause abrasion and grinding cracks.


8. Quenching deformation and cracking tendency: conventional quenching has small volume change, slight shape warping and distortion, and low abnormal deformation tendency. Conventional quenching has low cracking sensitivity and is not sensitive to quenching temperature and workpiece shape.